RHEPTS AC 0620F1 BRAZING RODS - 0.050IN X 1/8IN X 20IN - 0% SILVER (PACK OF 28)
RHEPTS AC 0620F1 BRAZING RODS - 0.050IN X 1/8IN X 20IN - 0% SILVER (PACK OF 28)
Harris® Brazing Alloy, 0.05 x 0.125 in Diameter, 20 in Length, 1310 deg F, 1460 deg F, Composition: 92 to 94% Copper, 6 to 8% Phosphorus
Why Create an Account?
- Ability to track orders
- More Options & Savings
- Amazing Customer Service
$55.97 / ea
Out of Stock
- Attributes
- Additional Information
- Features & Benefits
- Documents
Attributes
BrandRheem®
Alloy TypePhosCopper
Brazing Temperature Range1345 deg F-1500 deg F (729 deg C-816 deg C)
Chemical CompositionCopper Remainder%
Composition92 to 94% Copper, 6 to 8% Phosphorus
Diameter.050" x 1/8" (1.27mm x 3.18mm)
Electrical Conductivity (%IACS)9.9
Electrical Resistivity (Microhm/Cm)19.2
Fluidity Rating5
IndustryHVAC
Length20
Liquidus1460 deg F (793 deg C)
ModelNameHARRIS 0
Recommended FluxNo flux required for copper brazing. For brazing brass or copper to brass use Stay-Silv white flux. When flux is required, Harris Eco Smart boric acid free flux (powder or paste) is an excellent choice to promote sound brazed assemblies and comply with Eu
Recommended Joint Clearance.002"-.007" (.051mm-.178mm)
Size28 stick tube
Solidus1310 deg F (710 deg C)
Temperature Rating1310 deg F, 1460 deg F
Additional Information
ASME Section IIC SFA 5.8 BCuP-2|DIN 8513: L-CuP7|RoHS Compliant
Features & Benefits
- Economical choice for copper brazing Copper is self-fluxing Alloy flows quickly at brazing temperature so requires close joint tolerance Used in manual brazing applications Suitable for brazing brass Operators should avoid over heating the brass and use STAY-SILV® white brazing flux Not recommended for brazing steel or other ferrous base metals Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including HARRIS® 0, should not be used if the braze is exposed to sulfur or sulfur compounds in service Recommended joint clearance of 0.002" - 0.007" (0.05mm - 0.18mm) Conforms to the EU Reach & RoHS directive
RHEPTS AC 0620F1 BRAZING RODS - 0.050IN X 1/8IN X 20IN - 0% SILVER (PACK OF 28)
BrandRheem®
MFG #0620F1
Keller #1443967
My Part ##
Last Ordered#
$55.97 / ea